CN101233840B - Method for preparing a kind of tip of fishing rod - Google Patents
Method for preparing a kind of tip of fishing rod Download PDFInfo
- Publication number
- CN101233840B CN101233840B CN2008100081003A CN200810008100A CN101233840B CN 101233840 B CN101233840 B CN 101233840B CN 2008100081003 A CN2008100081003 A CN 2008100081003A CN 200810008100 A CN200810008100 A CN 200810008100A CN 101233840 B CN101233840 B CN 101233840B
- Authority
- CN
- China
- Prior art keywords
- cloth
- tail
- die
- solid
- rod
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a method for making a trainhead of a fishing rod, which comprises the following steps: a solid tail is prepared; a connection material tube is prepared; the solid tail and a module are connected by the connection tube and winded with material cloth and sent into a curing over to be heated and shaped. The method is suitable for making the trainhead by employing the materials such as glass fiber, carbon fiber or boron fiber. Compared with the traditional technology, the method for making the trainhead of the fishing rod has high intensity, good rigidity, simple preparation technique with low cost; in addition, the bonding of solid and hollow structures is difficult to break or creak, and the bonding place is easy to process.
Description
Technical field
The invention belongs to the manufacturing technology field of Fishing device, especially a kind of preparation method of kind of tip of fishing rod.
Background technology
The pole of telescopic fishing rod front end is referred to as the dragon and phoenix tail slightly, and its front end is thin, and the rear end is thick, and preceding half is solid, and back half is hollow, and the dragon and phoenix tail of this structure has guaranteed pole sensitivity slightly, has adjusted the center of gravity of pole body again.In the prior art, the manufacture craft of dragon and phoenix tail is that preceding half solid section is carried out, and back half hollow parts is also carried out, and two parts is bonded together again, and twines which floor glass fibre, carbon fiber or boron fibre solidifying and setting at bonding position and forms.Following problem appears in dragon and phoenix tail that this technology is made easily: 1, hollow and solid abutting edge easy fracture, though 2, hollow and solid abutting edge do not break after fishing for several times and obvious slight crack occurs, 3, hollow and solid abutting edge surface treatment effect is undesirable.
Summary of the invention
The objective of the invention is to overcome the deficiency of prior art, a kind of preparation method of kind of tip of fishing rod is provided, dragon and phoenix tail intensity height, pliability that this method is produced are good, hollow and solid abutting edge is not prone to slight crack and phenomenon of rupture, handle easily on the surface, abutting edge, and operation is simple, with low cost.
To achieve these goals, the present invention includes following steps:
(a) the solid tail of half before the preparation dragon and phoenix tail is produced the joint pin of diameter less than solid tail rear end in solid tail rear end;
(b) preparation connects the material pipe;
(c) use a kind of rod-like die, the rod-like die front end has the joint pin of diameter less than the rod-like die front end, solid tail rear end joint pin and mould front end joint pin is inserted to carry out in the material pipe be connected;
(d) material cloth is wrapped on the back segment and mould of the solid tail that connects, twines glassine paper or BOPP band in material cloth appearance then;
(e) send into hot briquetting in the curing oven after material cloth, glassine paper or BOPP band are wound, take out rod-like die, break away from glassine paper or BOPP band.
The length of described material pipe is 1.6～3.2cm, the length of the joint pin of solid tail rear end is 0.8～1.6cm, the length of the joint pin of rod-like die front end is 0.8～1.6cm, and wherein the length of material pipe equals the length sum of the joint pin of the length of joint pin of solid tail rear end and mould front end.
Described material cloth generally begins at solid tail and mould abutting edge leading portion 5～6cm place to twine, spool cloth after, the about 5～6cm of the back segment of solid tail by winding up in material cloth.
Material used in the present invention can be glass fibre, carbon fiber or boron fibre.Described material cloth can be glass fabric, carbon cloth or boron fibre cloth; Described solid tail can roll into to send into after the shape and add thermal finalization in the curing oven and make with glass fabric, carbon cloth or boron fibre cloth; Send into after described material pipe can be wrapped on the tubular die with glass fabric, carbon cloth or boron fibre cloth and add thermal finalization in the curing oven and make.
More smooth, more attractive in appearance for the surface that makes the dragon and phoenix tail, also need to carry out appearance behind taking-up rod-like die disengaging glassine paper or the BOPP and polish, spray paint, be coated with processing such as making lac varnish.
The preparation method of kind of tip of fishing rod of the present invention is compared with traditional handicraft, hollow and the solid junction of dragon and phoenix tail is not made bonding the forming in back to two parts, be on the basis of having made solid tail, to make hollow parts again, and material pipe support and connection in addition between two parts, dragon and phoenix tail intensity height, pliability that this method is made are good, hollowly and solid bondingly be not prone to slight crack or fracture, and the surface, abutting edge is handled easily also.In addition, this method also has advantages such as production process is simple, with low cost.
Description of drawings
The present invention will be further described in detail below in conjunction with the drawings and specific embodiments.
Fig. 1 is solid tail, rod-like die and material tubular construction schematic diagram;
Fig. 2 is the structural representation after solid tail and rod-like die are connected with the material pipe;
Fig. 3 is the mode schematic diagram that twines material cloth on the back segment of solid tail and rod-like die;
Embodiment
Embodiment 1: as shown in Figure 1, 2, 3, the present invention includes following steps:
(a) prepare the solid tail 1 of half before the dragon and phoenix tail with carbon cloth, to produce diameter be the joint pin 2 of 1cm less than solid tail 1 rear end and length to 1 end behind solid tail;
(b) prepare the connection material pipe 5 that length is 2cm with carbon cloth;
(c) use a kind of rod-like die 4, it is joint pins 3 of 1cm less than rod-like die 4 front end length that rod-like die 4 front ends have diameter, solid tail 1 rear end joint pin 2 is inserted to carry out in the material pipe 5 with mould 4 front end joint pins 3 be connected;
(d) begin to twine carbon cloth at solid tail and mould abutting edge leading portion 6cm place, carbon cloth 6 is wrapped on the back segment and mould 4 of solid tail 1, twine glassine paper or BOPP band in the carbon cloth appearance then;
(e) send into hot briquetting in the curing oven after carbon cloth 6, glassine paper or BOPP band are wound, take out rod-like die 4, break away from glassine paper or BOPP band, carry out appearance again and polish, spray paint, be coated with processing such as making lac varnish.
Embodiment 2: as shown in Figure 1, 2, 3, the present invention includes following steps:
(a) prepare the solid tail 1 of half before the dragon and phoenix tail with glass fabric, to produce diameter be the joint pin 2 of 1.2cm less than solid tail 1 rear end and length to 1 end behind solid tail;
(b) prepare the connection material pipe 5 that length is 2.4cm with glass fabric;
(c) use a kind of rod-like die 4, it is joint pins 3 of 1.2cm less than rod-like die 4 front end length that rod-like die 4 front ends have diameter, solid tail 1 rear end joint pin 2 is inserted to carry out in the material pipe 5 with mould 4 front end joint pins 3 be connected;
(d) begin to twine glass fabric at solid tail and mould abutting edge leading portion 5cm place, glass fabric 6 is wrapped on the back segment and mould 4 of solid tail 1, twine glassine paper or BOPP band in the glass fabric appearance then;
(e) send into hot briquetting in the curing oven after glass fabric 6, glassine paper or BOPP band are wound, take out rod-like die 4, break away from glassine paper or BOPP band, carry out appearance again and polish, spray paint, be coated with processing such as making lac varnish.
Embodiment 3: as shown in Figure 1, 2, 3, the present invention includes following steps:
(a) prepare the preceding solid tail 1 of half of dragon and phoenix tail with boron fibre cloth, producing diameter in solid tail 1 rear end is the joint pin 2 of 1.3cm less than solid tail 1 rear end and length;
(b) prepare the connection material pipe 5 that length is 2.6cm with boron fibre cloth;
(c) use a kind of rod-like die 4, it is joint pins 3 of 1.3cm less than rod-like die 4 front end length that rod-like die 4 front ends have diameter, solid tail 1 rear end joint pin 2 is inserted to carry out in the material pipe 5 with mould 4 front end joint pins 3 be connected;
(d) begin to twine boron fibre cloth at solid tail and mould abutting edge leading portion 5.5cm place, boron fibre cloth 6 is wrapped on the back segment and mould 4 of solid tail 1, twine glassine paper or BOPP band in boron fibre cloth appearance then;
(e) send into hot briquetting in the curing oven after boron fibre cloth 6, glassine paper or BOPP band are wound, take out rod-like die 4, break away from glassine paper or BOPP band, carry out appearance again and polish, spray paint, be coated with processing such as making lac varnish.
Claims (5)
1. the preparation method of a kind of tip of fishing rod, it comprises the steps:
(a) the solid tail of half (1) before the preparation dragon and phoenix tail is produced the joint pin (2) of diameter less than solid tail (1) rear end in solid tail (1) rear end;
(b) preparation connects material pipe (5);
(c) use a kind of rod-like die (4), rod-like die (4) front end has the joint pin (3) of diameter less than rod-like die (4) front end, solid tail (1) rear end joint pin (2) and mould (4) front end joint pin (3) is inserted to carry out in the material pipe (5) be connected;
(d) material cloth (6) is wrapped on the back segment and mould (4) of the solid tail (1) that connects, twines glassine paper or BOPP band in material cloth (6) appearance then;
(e) send into hot briquetting in the curing oven after material cloth (6), glassine paper or BOPP band are wound, take out rod-like die (4), break away from glassine paper or BOPP band.
2. according to the preparation method of the described kind of tip of fishing rod of claim 1, it is characterized in that: the length of described material pipe (5) is 1.6～3.2cm, the length of the joint pin (2) of solid tail (1) rear end is 0.8～1.6cm, the length of the joint pin (3) of rod-like die (4) front end is 0.8～1.6cm, and wherein the length of material pipe (5) equals the length sum of the joint pin (3) of the length of joint pin (2) of solid tail (1) rear end and mould (4) front end.
3. according to the preparation method of claim 1 or 2 described kind of tip of fishing rod, it is characterized in that: described material cloth begins to twine at solid tail and mould abutting edge leading portion 5～6cm place.
4. according to the preparation method of claim 1 or 2 described kind of tip of fishing rod, it is characterized in that: described material cloth (6) is glass fabric, carbon cloth or boron fibre cloth; Described solid tail (1) rolls into to send into after the shape with glass fabric, carbon cloth or boron fibre cloth and adds thermal finalization in the curing oven and make; Send into after described material pipe (5) is wrapped on the tubular die with glass fabric, carbon cloth or boron fibre cloth and add thermal finalization in the curing oven and make.
5. according to the preparation method of the described kind of tip of fishing rod of claim 3, it is characterized in that: described material cloth (6) is glass fabric, carbon cloth or boron fibre cloth; Described solid tail (1) rolls into to send into after the shape with glass fabric, carbon cloth or boron fibre cloth and adds thermal finalization in the curing oven and make; Send into after described material pipe (5) is wrapped on the tubular die with glass fabric, carbon cloth or boron fibre cloth and add thermal finalization in the curing oven and make.