CN109810590A - A kind of indoor wall repairs aerosol and preparation method thereof - Google Patents
A kind of indoor wall repairs aerosol and preparation method thereof Download PDFInfo
- Publication number
- CN109810590A CN109810590A CN201910101668.8A CN201910101668A CN109810590A CN 109810590 A CN109810590 A CN 109810590A CN 201910101668 A CN201910101668 A CN 201910101668A CN 109810590 A CN109810590 A CN 109810590A
- Authority
- CN
- China
- Prior art keywords
- aerosol
- pigment
- repairs
- indoor wall
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of indoor walls to repair aerosol, which is characterized in that including the following raw material: resin, solvent, levelling agent, dispersing agent, propellant.The present invention, which can both repair rapidly scratching etc. on metope, influences beautiful worry,, fanout free region pollution-free to people simultaneously, safety and environmental protection, it is good that product has a spraying sprayability, the high feature of emission rate, and color film is dry rapid, adhesive force is strong, the color rich in color for being suitable for different indoor walls, alternative strong, repairing effect is good.
Description
Technical field
The invention belongs to household chemicals technical fields, and in particular to a kind of indoor wall repairs aerosol and its preparation side
Method.
Background technique
In recent years, with economic sustainable growth, people's lives level is improved rapidly.People are to indoor environment
It is required that higher and higher, indoor wall is easy to be scratched in daily life, and discoloration is to influence working efficiency and mood.
In conclusion developing the urgent need that one kind indoor wall mending paint simple and easy to use has become market.
Summary of the invention
The purpose of the present invention is to provide a kind of indoor walls to repair aerosol and preparation method thereof.
The technical solution used in the present invention is:
A kind of indoor wall repairs aerosol, which is characterized in that the main product made of the following raw material: film forming agent, molten
Agent, deionized water, pigment, dispersing agent, defoaming agent, propellant.
Including the following raw material preferably, according to the mass fraction: 10-15 parts of film forming agent, 5-15 parts of solvent, 5-10 parts of pigment,
0.4-5 parts of dispersing agent, 0.5-5 parts of defoaming agent, 30-50 parts of deionized water, 20-40 parts of propellant.
Preferably, the film forming agent is one of acrylic acid modified resin, polyurethane resin, alkyd resin or a variety of
Combination.
Preferably, the solvent is one of 95% ethyl alcohol, dehydrated alcohol, propylene glycol, isopropanol, white oil or a variety of
Combination.
Preferably, the pigment be one of inorganic pigment, pearlescent pigment, fluorescent pigment, glitter powder, chameleon or
Multiple combinations.
Preferably, the dispersing agent is white carbon black, talcum powder, bentonite, diatomite, zinc stearate, Bentone 38
One of or multiple combinations.
Preferably, the defoaming agent is GPE20, in tributyl phosphate, polyether-modified silicon defoaming agent, organic silicon defoamer
One or more combinations.
A kind of indoor wall repairs the preparation method of aerosol, which comprises the steps of:
(1) film forming agent is added in solvent, stirring and dissolving, add pigment or dispersible pigment color paste, dispersing agent, defoaming agent,
Deionized water is uniformly mixed, and obtains agent liquid needed for product；
(2) agent liquid is fitted into inhalator jar, then be filled in proportion propellant to get.
Preferably, the dispersible pigment color paste, prepares by the following method: pigment, dispersing agent, solvent and deionized water are put into
It prepares in pot, is mixed evenly, then, this feed liquid is gone again and makees further dispersion with colloid mill, the feed liquid of dispersion is via filter
Bag filtering to get.
It is further preferred that the pigment is the combination of one or both of inorganic pigment or fluorescent pigment.
Appropriate amount of essence can also be added in the present invention.
Inventive formulation design principle: with a kind of film forming agent close to metope emulsion paint, suitable color is deployed, is added and closes
Suitable solvent, deionized water, defoaming agent, dispersing agent are made by the production method of aerosol, and suitable propellant is added,
Its atomizing effect is set to meet requirement.
Acrylic acid modified resin in the present invention is with moral resin 3AH0545, index are as follows: solid content: 45%, viscosity:
300—2000cps/30℃；Feature: versatile, gloss is high, excellent water resistance, chemical-resistant.
The beneficial effects of the present invention are:
The prepared indoor wall of the present invention repairs aerosol, can both repair rapidly scratching etc. on metope influence it is beautiful
Worry, while, fanout free region pollution-free to people, safety and environmental protection realize following index, effect simultaneously in actual use:
1, color variety multiplicity, it is rich and varied, give user to provide more selections, it is easy to use, covering power is good, can have
Effect repairing metope problem；
2, nonirritant peculiar smell can also like adjustment odor type smell according to self；
3, adhesive force is good, realizes that nothing falls off；
4, emission rate >=95%, no waste sufficiently use；
5, product (25 DEG C) pressure is less than 0.8Mpa；
6, rate of drying is very fast, and repetitive operation is facilitated to use；
The present invention has that spraying sprayability is good, and the high feature of emission rate, color film is dry rapidly, and adhesive force is strong, rich in color
It is suitable for the color of different indoor walls, alternative strong, repairing effect is good.
Detailed description of the invention
Fig. 1 is to use picture before product of the present invention.
Fig. 2 is to use picture after product of the present invention.
Specific embodiment
Below with reference to embodiment, the present invention is further illustrated.
Embodiment 1
Fluorescent white metope repairs aerosol
Raw material: propylene acid modified resin 12kg, fluorescence white pigments 8kg, talcum powder 2.4kg, white carbon black 0.5kg, 95% second
Alcohol 10kg, propylene glycol 1kg, GPE20 0.5Kg, deionized water 35.5Kg, essence 0.1kg, dimethyl ether 30kg.
The preparation method is as follows:
(1) pre-dispersed: 95% ethyl alcohol 10kg to be put into pill tank, placing into power is 22-35KW, frequency conversion 0-3000
Turn/the stirring dispersion machine of min, slowly starts stirring, fluorescence white pigments 8kg, the talcum powder 2.4kg of accurate measurement are put into when stirring
It with white carbon black 0.5kg, mixes, obtains heavy colour slurry, subsequent grinding can be ready for use on and used.
(2) grinding distribution: the mill base after will be pre-dispersed is dispersed by colloid mill equipment, and the feed liquid of dispersion is through 100 mesh
Sock filtration is used in this, as pigment underflow used in product.During colloid mill carries out homogenous disperse to underflow agent liquid, observation
Dispersion needs to adjust colloid mill spacing immediately or circulation of the feed liquid in colloid mill is appropriately extended if dispersion is bad
Time, with the dispersion effect ensured.
(3) agent liquid is prepared: propylene glycol 1kg being added and is prepared in pot, stirring is started, 12kg acrylic acid tree is added when stirring
Rouge mixes, after completely dissolution, then ground pigment underflow is added and is prepared in pot, continues high speed dispersion and stirs 30 minutes, it
Afterwards, GPE20 0.5Kg is added, deionized water 35.5Kg, 0.1kg essence stirs 5 minutes, is uniformly dispersed and obtains agent material.
(4) it fills tank finished product: by the production method of aerosol products, after filling dose of liquid, being filled with propellant dimethyl ether in proportion,
Under room temperature, pressure 0.35-0.8Mpa can be obtained indoor wall repairing aerosol.
Embodiment 2
Pearlescent white indoor wall repairs aerosol
Raw material: polyurethane resin 15kg, 95% ethyl alcohol 8kg, flashing pearl 6kg, white carbon black 0.4kg, polyether-modified silicon disappear
Infusion 0.5kg, deionized water 45kg, essence 0.1kg, dimethyl ether 25kg.
The preparation method is as follows:
(1) agent liquid is prepared: deionized water 45kg being added and is prepared in pot, stirring is started, the slow 15kg that is added when stirring gathers
The materials such as urethane resin, 95% ethyl alcohol of 8kg, 6kg flashing pearl powder, 0.4kg white carbon black, the polyether-modified silicon defoaming agent of 0.5kg,
After elementary mixing, high speed dispersion is stirred 30 minutes, and then 0.1kg essence is added, and is stirred 5 minutes, is uniformly dispersed and obtains agent
Material.
(2) tank finished product is filled: with embodiment 1.
Embodiment 3
White indoor wall repairs aerosol
Raw material: alkyd resin 13kg, 95% ethyl alcohol 8kg, white oil 0.5kg, titanium dioxide 6kg, bentonite 1.5kg, stearic acid
Zinc 0.4kg, organic silicon defoamer 0.5kg, deionized water 42kg, essence 0.1kg, dimethyl ether 28kg.
The preparation method is as follows:
(1) agent liquid is prepared: deionized water 42kg is added and is prepared in pot, stirring is started, it is slow to be added when stirring: alkyd tree
Rouge 13kg, 8kg95% ethyl alcohol, white oil 0.5kg, titanium dioxide 6kg, bentonite 1.5kg, zinc stearate 0.4kg, organic silicon defoamer
The materials such as 0.5kg, after elementary mixing, high speed dispersion is stirred 30 minutes, and then 0.1kg essence is added, and is stirred 5 minutes, dispersion
Uniformly obtain agent material.
(2) tank finished product is filled: with embodiment 1.
Embodiment 4
Pearlescent white indoor wall repairs aerosol
Raw material: polyurethane resin 5kg, alkyd resin 5kg, dehydrated alcohol 8kg, isopropanol 7kg, chameleon 5kg, diatomite
5kg, tributyl phosphate 3kg, deionized water 30kg, essence 0.1kg, dimethyl ether 20kg.
The preparation method is as follows:
(1) agent liquid is prepared: deionized water 30kg is added and is prepared in pot, stirring is started, it is slow that the poly- ammonia of 5kg is added when stirring
Ester resin, alkyd resin 5kg, dehydrated alcohol 8kg, isopropanol 7kg, chameleon 5kg, diatomite 5kg, tributyl phosphate 3kg etc.
Material, after elementary mixing, high speed dispersion is stirred 30 minutes, and then 0.1kg essence is added, and is stirred 5 minutes, is uniformly dispersed
Agent material out.
(2) tank finished product is filled: with embodiment 1.
Embodiment 5
Pearlescent white indoor wall repairs aerosol
Raw material: polyurethane resin 15kg, 95% ethyl alcohol 5kg, 38 3kg of glitter powder 10kg, Bentone, polyether-modified silicon
Defoaming agent 2kg, tributyl phosphate 3kg, deionized water 50kg, dimethyl ether 40kg.
The preparation method is as follows:
(1) agent liquid is prepared: deionized water 50kg being added and is prepared in pot, stirring is started, the slow 15kg that is added when stirring gathers
Urethane resin, 5kg95% ethyl alcohol, 38 3kg of glitter powder 10kg, Bentone, polyether-modified silicon defoaming agent 2kg, tributyl phosphate
3kg, etc. materials, after elementary mixing, high speed dispersion is stirred 30 minutes, is stirred 5 minutes later, is uniformly dispersed and obtains agent material.
(2) tank finished product is filled: with embodiment 1.
Performance test
Every physical and chemical, functional attributes method of inspection:
1. smell: product are heard.
2. pressure (25 DEG C, Mpa): being carried out by " test of internal pressure " in GB/T14449-2008 aerosol products test method
It examines.
3. emission rate (%): being examined by " test of emission rate " in GB/T14449-2008 aerosol products test method
It tests.
4. adhesive force: by application method, correctly product is uniformly sprayed on a tinplate small iron plate by spray pattern, 30 points
Clock touches film surface after color film is completely dried, with finger, to be that adhesive force is good without decoloration.
5. surface drying time (25 DEG C, min): referring to " dry tack free in GB1728-79 paint film putty membrane drying time measuring method
The fingers-touch method of chronometry " touches color film surface with finger, such as feels that some are tacky, but stick to the finger without toner, that is, recognize
For dry tack free.
The quality index for the product that embodiment 1-3 is prepared is as shown in table 1.
Table 1
| Index parameter | Embodiment 1 | Embodiment 2 | Embodiment 3 |
| Smell | Free from extraneous odour | Free from extraneous odour | Free from extraneous odour |
| Pressure (25 DEG C, Mpa) | < 0.8 | < 0.8 | < 0.8 |
| Emission rate (%) | ≥95 | ≥95 | ≥95 |
| Adhesive force | It is good | Preferably | Generally |
| Surface drying time (25 DEG C, min) | < 5 | < 4 | < 6 |
From the data of table 1, attached drawing 1 and attached drawing 2: it is fast that indoor wall of the invention repairs aerosol tool Coloured film drying
Speed, the advantages that adhesive force is strong, the color rich in color for being suitable for different indoor walls, alternative strong, repairing effect is excellent
Characteristic can meet the needs of consumer's convenient and simple reparation indoor wall wish.
Above-described embodiment is merely illustrative of the technical solution of the present invention and is not intended to limit it, all without departing from the present invention
Any modification of spirit and scope or equivalent replacement should all cover the range in technical solution of the present invention.
Claims (10)
1. a kind of indoor wall repairs aerosol, which is characterized in that the main product made of the following raw material: film forming agent, solvent,
Deionized water, pigment, dispersing agent, defoaming agent, propellant.
2. a kind of indoor wall according to claim 1 repairs aerosol, which is characterized in that according to the mass fraction, including
The following raw material: 10-15 parts of film forming agent, 5-15 parts of solvent, 5-10 parts of pigment, 0.4-5 parts of dispersing agent, 0.5-5 parts of defoaming agent, go from
Sub- water 30-50 parts, 20-40 parts of propellant.
3. a kind of indoor wall according to claim 1 or 2 repairs aerosol, which is characterized in that the film forming agent is
One of acrylic acid modified resin, polyurethane resin, alkyd resin or multiple combinations.
4. a kind of indoor wall according to claim 1 or 2 repairs aerosol, which is characterized in that the solvent is
One of 95% ethyl alcohol, dehydrated alcohol, propylene glycol, isopropanol, white oil or multiple combinations.
5. a kind of indoor wall according to claim 1 or 2 repairs aerosol, which is characterized in that the pigment is nothing
One of machine pigment, pearlescent pigment, fluorescent pigment, glitter powder, chameleon or multiple combinations.
6. a kind of indoor wall according to claim 1 or 2 repairs aerosol, which is characterized in that the dispersing agent is
One of white carbon black, talcum powder, bentonite, diatomite, zinc stearate, Bentone 38 or multiple combinations.
7. a kind of indoor wall according to claim 1 or 2 repairs aerosol, which is characterized in that the defoaming agent is
One of GPE20, tributyl phosphate, polyether-modified silicon defoaming agent, organic silicon defoamer or multiple combinations.
8. the preparation method that a kind of indoor wall repairs aerosol, which comprises the steps of:
(1) film forming agent is added in solvent, stirring and dissolving, add pigment or dispersible pigment color paste, dispersing agent, defoaming agent, go from
Sub- water, is uniformly mixed, and obtains agent liquid needed for product；
(2) agent liquid is fitted into inhalator jar, then be filled in proportion propellant to get.
9. a kind of indoor wall according to claim 8 repairs aerosol, which is characterized in that the dispersible pigment color paste, by
Following method preparation: pigment, dispersing agent, solvent being put into and prepared in pot, is mixed evenly, and then, by this feed liquid, row is used again
Colloid mill makees further dispersion, the feed liquid of dispersion via sock filtration to get.
10. indoor wall according to claim 9 repairs aerosol, which is characterized in that the pigment is inorganic pigment
Or one or both of fluorescent pigment combination.