CN109749145B - 一种改性木质素/壳聚糖橡胶增强填料的制备方法 - Google Patents
一种改性木质素/壳聚糖橡胶增强填料的制备方法 Download PDFInfo
- Publication number
- CN109749145B CN109749145B CN201811433559.8A CN201811433559A CN109749145B CN 109749145 B CN109749145 B CN 109749145B CN 201811433559 A CN201811433559 A CN 201811433559A CN 109749145 B CN109749145 B CN 109749145B
- Authority
- CN
- China
- Prior art keywords
- lignin
- chitosan
- solution
- reaction
- drying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供了一种改性木质素/壳聚糖橡胶增强填料的制备方法，包括以下步骤：S1.木质素的纯化；S2.木质素的氧化和磺化；S3.木质素/壳聚糖的复合；S4.双硬脂酰乙基环氧丙基氯化铵的合成；S5.改性木质素/壳聚糖的制备。本发明的改性木质素/壳聚糖橡胶增强填料具有以下优点：通过壳聚糖和木质素的改性，进一步提高了反应活性，显著提高橡胶的力学性能,同时二者具有很好的协同作用。
Description
技术领域
本发明涉及橡胶填料领域，具体涉及一种改性木质素/壳聚糖橡胶增强填料的制备方法。
背景技术
木质素存在于大部分陆地植物木质部中，与纤维素和半纤维素构成植物的骨架，是一种复杂的高分子化合物。一般认为，木质素的基本结构单元是苯丙烷，共有3种基本结构：愈创木基丙烷、紫丁香基丙烷和对羟苯基丙烷。木质素的结构单元上有许多功能基团，如芳香基、酚羟基、醇羟基、羧基等，这些功能基团的存在使木质素具有很强的反应活性。木质素可作为添加剂用于橡胶中，其分子中的酚基和羧基等基团，不仅能提高材料的防老化效果，还能提高材料的物理机械性能。
壳聚糖(CS)是甲壳素经过不同程度的脱乙酰作用得到的可再生资源。CS分子有活泼的羟基和氨基,具有较强的化学反应能力,易发生水解、烷基化、酰基化、羟基化、接枝、季铵盐化等反应,可生成各种具有不同性能的衍生物，具备与其他物质结合、赋予共聚物以自身特性的现实基础。
天然橡胶(NR)一般为由巴西三叶橡胶采集得到的经系列加工得到的浓缩天然胶乳或颗粒胶,具有优异的综合性能。尽管CS与NR均为材料研究中非常热门的具有独特性能和潜在利用价值的天然高分子,但两者相互混合赋予新复合物以各自特性却非简单混合即可实现。本发明将对CS作为增强材料的改性。
发明内容
要解决的技术问题：本发明的目的是提供改性木质素/壳聚糖橡胶增强填料的制备方法，制备得到的填料增强效果好。
技术方案：一种改性木质素/壳聚糖橡胶增强填料的制备方法，包括以下步骤：
S1.木质素的纯化：将木质素溶解于二氧六环-水溶液中，离心得到离心液，在离心液中滴加乙醚，得到沉淀，将沉淀洗涤干燥，得到纯化的木质素；
S2.木质素的氧化和磺化：将木质素加入至含有氢氧化钠的去离子水中，加热至木质素完全溶解，调节溶液的pH值至5，然后加入过氧化氢和硫酸亚铁反应，待达到反应时间后加碱调节溶液pH至9，加入甲醛和二乙醇胺，在70-80℃下反应后，再升温至90℃，加入亚硫酸钠，反应完全后，加酸使得木质素沉淀，洗涤干燥得到氧化磺化的木质素；
S3.木质素/壳聚糖的复合：将步骤S2中制备的木质素溶解于二氧六环-水的溶液，壳聚糖溶解于醋酸水溶液中，将两种溶液混合，加入戊二醛交联，最后在室温下抽滤，洗涤，并在红外箱中烘干，得到木质素/壳聚糖复合粉末；
S4.双硬脂酰乙基环氧丙基氯化铵的合成：将双硬脂酰基二乙烯三胺和苯加热回流反应，并滴加环氧氯丙烷，搅拌至反应完全后蒸发出苯和过量的环氧氯丙烷，得到双硬脂酰胺乙基环氧丙基氯化铵；
S5.改性木质素/壳聚糖的制备：将步骤S3制备的木质素/壳聚糖复合粉末加入至去离子水水中，加热搅拌至完全溶解，调节pH为10，然后滴加双硬脂酰胺乙基环氧丙基氯化铵，搅拌下反应完全，再抽滤干燥，得到改性木质素/壳聚糖。
进一步的，所述步骤S1中二氧六环-水的体积比为9:1。
进一步的，所述步骤S3中将步骤S2中制备的木质素溶解于二氧六环-水的溶液配置浓度为3％的溶液，壳聚糖溶解于2-3％醋酸水溶液中配置浓度为2-5％的溶液，将两种溶液按体积比1:0.5-1.5混合，加入0.3-0.8％的戊二醛交联，最后在室温下抽滤，洗涤，并在红外箱中烘干，得到木质素/壳聚糖复合粉末。
进一步的，所述步骤S4中双硬脂酰基二乙烯三胺和环氧氯丙烷溶解于苯中的浓度为0.8-1mol/L。
进一步的，所述步骤S5中将步骤S3制备的木质素/壳聚糖复合粉末加入至去离子水水中配置成浓度为0.5mol/L的溶液，加热至40-50℃搅拌至完全溶解，调节pH为10，然后滴加双硬脂酰胺乙基环氧丙基氯化铵，搅拌下反应1-3h，再抽滤干燥，得到改性木质素/壳聚糖。
有益效果：本发明的改性木质素/壳聚糖橡胶增强填料具有以下优点：通过壳聚糖和木质素的改性，进一步提高了反应活性，显著提高橡胶的力学性能,同时二者具有很好的协同作用。
具体实施方式
实施例1
一种改性木质素/壳聚糖橡胶增强填料的制备方法，包括以下步骤：
S1.木质素的纯化：将5倍重量份木质素溶解于100倍重量份的二氧六环-水溶液中，二氧六环-水的体积比为9:1，离心得到离心液，在离心液中滴加乙醚，得到沉淀，将沉淀洗涤干燥，得到纯化的木质素；
S2.木质素的氧化和磺化：将木质素加入至含有氢氧化钠的去离子水中，加热至木质素完全溶解，调节溶液的pH值至5，然后加入过氧化氢和硫酸亚铁反应，待达到反应时间后加碱调节溶液pH至9，加入甲醛和二乙醇胺，在70℃下反应后，再升温至90℃，加入亚硫酸钠，反应完全后，加酸使得木质素沉淀，洗涤干燥得到氧化磺化的木质素；
S3.木质素/壳聚糖的复合：将步骤S2中制备的木质素溶解于二氧六环-水的溶液配置浓度为3％的溶液，壳聚糖溶解于2％醋酸水溶液中配置浓度为5％的溶液，将两种溶液按体积比1:0.5混合，加入0.3％的戊二醛交联，最后在室温下抽滤，洗涤，并在红外箱中烘干，得到木质素/壳聚糖复合粉末；
S4.双硬脂酰乙基环氧丙基氯化铵的合成：将双硬脂酰基二乙烯三胺和苯加热回流反应，并滴加环氧氯丙烷，双硬脂酰基二乙烯三胺和环氧氯丙烷溶解于苯中的浓度为0.8mol/L，搅拌至反应完全后蒸发出苯和过量的环氧氯丙烷，得到双硬脂酰胺乙基环氧丙基氯化铵；
S5.改性木质素/壳聚糖的制备：将步骤S3制备的木质素/壳聚糖复合粉末加入至去离子水水中配置成浓度为0.5mol/L的溶液，加热至40℃搅拌至完全溶解，调节pH为10，然后滴加双硬脂酰胺乙基环氧丙基氯化铵，搅拌下反应1h，再抽滤干燥，得到改性木质素/壳聚糖。
实施例2
一种改性木质素/壳聚糖橡胶增强填料的制备方法，包括以下步骤：
S1.木质素的纯化：将10倍重量份木质素溶解于100倍重量份的二氧六环-水溶液中，二氧六环-水的体积比为9:1，离心得到离心液，在离心液中滴加乙醚，得到沉淀，将沉淀洗涤干燥，得到纯化的木质素；
S2.木质素的氧化和磺化：将木质素加入至含有氢氧化钠的去离子水中，加热至木质素完全溶解，调节溶液的pH值至5，然后加入过氧化氢和硫酸亚铁反应，待达到反应时间后加碱调节溶液pH至9，加入甲醛和二乙醇胺，在80℃下反应后，再升温至90℃，加入亚硫酸钠，反应完全后，加酸使得木质素沉淀，洗涤干燥得到氧化磺化的木质素；
S3.木质素/壳聚糖的复合：将步骤S2中制备的木质素溶解于二氧六环-水的溶液配置浓度为3％的溶液，壳聚糖溶解于3％醋酸水溶液中配置浓度为2％的溶液，将两种溶液按体积比1:1.5混合，加入0.8％的戊二醛交联，最后在室温下抽滤，洗涤，并在红外箱中烘干，得到木质素/壳聚糖复合粉末；
S4.双硬脂酰乙基环氧丙基氯化铵的合成：将双硬脂酰基二乙烯三胺和苯加热回流反应，并滴加环氧氯丙烷，双硬脂酰基二乙烯三胺和环氧氯丙烷溶解于苯中的浓度为1mol/L，搅拌至反应完全后蒸发出苯和过量的环氧氯丙烷，得到双硬脂酰胺乙基环氧丙基氯化铵；
S5.改性木质素/壳聚糖的制备：将步骤S3制备的木质素/壳聚糖复合粉末加入至去离子水水中配置成浓度为0.5mol/L的溶液，加热至50℃搅拌至完全溶解，调节pH为10，然后滴加双硬脂酰胺乙基环氧丙基氯化铵，搅拌下反应3h，再抽滤干燥，得到改性木质素/壳聚糖。
实施例3
一种改性木质素/壳聚糖橡胶增强填料的制备方法，包括以下步骤：
S1.木质素的纯化：将6倍重量份木质素溶解于100倍重量份的二氧六环-水溶液中，二氧六环-水的体积比为9:1，离心得到离心液，在离心液中滴加乙醚，得到沉淀，将沉淀洗涤干燥，得到纯化的木质素；
S2.木质素的氧化和磺化：将木质素加入至含有氢氧化钠的去离子水中，加热至木质素完全溶解，调节溶液的pH值至5，然后加入过氧化氢和硫酸亚铁反应，待达到反应时间后加碱调节溶液pH至9，加入甲醛和二乙醇胺，在75℃下反应后，再升温至90℃，加入亚硫酸钠，反应完全后，加酸使得木质素沉淀，洗涤干燥得到氧化磺化的木质素；
S3.木质素/壳聚糖的复合：将步骤S2中制备的木质素溶解于二氧六环-水的溶液配置浓度为3％的溶液，壳聚糖溶解于2.2％醋酸水溶液中配置浓度为3-4％的溶液，将两种溶液按体积比1:1.2混合，加入0.4％的戊二醛交联，最后在室温下抽滤，洗涤，并在红外箱中烘干，得到木质素/壳聚糖复合粉末；
S4.双硬脂酰乙基环氧丙基氯化铵的合成：将双硬脂酰基二乙烯三胺和苯加热回流反应，并滴加环氧氯丙烷，双硬脂酰基二乙烯三胺和环氧氯丙烷溶解于苯中的浓度为0.9mol/L，搅拌至反应完全后蒸发出苯和过量的环氧氯丙烷，得到双硬脂酰胺乙基环氧丙基氯化铵；
S5.改性木质素/壳聚糖的制备：将步骤S3制备的木质素/壳聚糖复合粉末加入至去离子水水中配置成浓度为0.5mol/L的溶液，加热至45℃搅拌至完全溶解，调节pH为10，然后滴加双硬脂酰胺乙基环氧丙基氯化铵，搅拌下反应2h，再抽滤干燥，得到改性木质素/壳聚糖。
实施例4
一种改性木质素/壳聚糖橡胶增强填料的制备方法，包括以下步骤：
S1.木质素的纯化：将9倍重量份木质素溶解于100倍重量份的二氧六环-水溶液中，二氧六环-水的体积比为9:1，离心得到离心液，在离心液中滴加乙醚，得到沉淀，将沉淀洗涤干燥，得到纯化的木质素；
S2.木质素的氧化和磺化：将木质素加入至含有氢氧化钠的去离子水中，加热至木质素完全溶解，调节溶液的pH值至5，然后加入过氧化氢和硫酸亚铁反应，待达到反应时间后加碱调节溶液pH至9，加入甲醛和二乙醇胺，在80℃下反应后，再升温至90℃，加入亚硫酸钠，反应完全后，加酸使得木质素沉淀，洗涤干燥得到氧化磺化的木质素；
S3.木质素/壳聚糖的复合：将步骤S2中制备的木质素溶解于二氧六环-水的溶液配置浓度为3％的溶液，壳聚糖溶解于2.8％醋酸水溶液中配置浓度为3-4％的溶液，将两种溶液按体积比1:0.8混合，加入0.6％的戊二醛交联，最后在室温下抽滤，洗涤，并在红外箱中烘干，得到木质素/壳聚糖复合粉末；
S4.双硬脂酰乙基环氧丙基氯化铵的合成：将双硬脂酰基二乙烯三胺和苯加热回流反应，并滴加环氧氯丙烷，双硬脂酰基二乙烯三胺和环氧氯丙烷溶解于苯中的浓度为0.8mol/L，搅拌至反应完全后蒸发出苯和过量的环氧氯丙烷，得到双硬脂酰胺乙基环氧丙基氯化铵；
S5.改性木质素/壳聚糖的制备：将步骤S3制备的木质素/壳聚糖复合粉末加入至去离子水水中配置成浓度为0.5mol/L的溶液，加热至50℃搅拌至完全溶解，调节pH为10，然后滴加双硬脂酰胺乙基环氧丙基氯化铵，搅拌下反应3h，再抽滤干燥，得到改性木质素/壳聚糖。
实施例5
一种改性木质素/壳聚糖橡胶增强填料的制备方法，包括以下步骤：
S1.木质素的纯化：将8倍重量份木质素溶解于100倍重量份的二氧六环-水溶液中，二氧六环-水的体积比为9:1，离心得到离心液，在离心液中滴加乙醚，得到沉淀，将沉淀洗涤干燥，得到纯化的木质素；
S2.木质素的氧化和磺化：将木质素加入至含有氢氧化钠的去离子水中，加热至木质素完全溶解，调节溶液的pH值至5，然后加入过氧化氢和硫酸亚铁反应，待达到反应时间后加碱调节溶液pH至9，加入甲醛和二乙醇胺，在78℃下反应后，再升温至90℃，加入亚硫酸钠，反应完全后，加酸使得木质素沉淀，洗涤干燥得到氧化磺化的木质素；
S3.木质素/壳聚糖的复合：将步骤S2中制备的木质素溶解于二氧六环-水的溶液配置浓度为3％的溶液，壳聚糖溶解于2.5％醋酸水溶液中配置浓度为3.5％的溶液，将两种溶液按体积比1:1混合，加入0.5％的戊二醛交联，最后在室温下抽滤，洗涤，并在红外箱中烘干，得到木质素/壳聚糖复合粉末；
S4.双硬脂酰乙基环氧丙基氯化铵的合成：将双硬脂酰基二乙烯三胺和苯加热回流反应，并滴加环氧氯丙烷，双硬脂酰基二乙烯三胺和环氧氯丙烷溶解于苯中的浓度为0.9mol/L，搅拌至反应完全后蒸发出苯和过量的环氧氯丙烷，得到双硬脂酰胺乙基环氧丙基氯化铵；
S5.改性木质素/壳聚糖的制备：将步骤S3制备的木质素/壳聚糖复合粉末加入至去离子水水中配置成浓度为0.5mol/L的溶液，加热至48℃搅拌至完全溶解，调节pH为10，然后滴加双硬脂酰胺乙基环氧丙基氯化铵，搅拌下反应2h，再抽滤干燥，得到改性木质素/壳聚糖。
对比例1
不添加木质素，其余和实施例1相同。
对比例2
不添加壳聚糖，其余和实施例1相同。
橡胶试样的配方如下：天然橡胶110份，改性木质素/壳聚糖橡胶增强填料20份，炭黑30份，硬脂酸5份，ZnO3份，防老剂5份，硫磺2份，硫化促进剂2份。
物理性能：邵尔A型硬度按GB/T 531测定，拉伸性能和撕裂强度分别按GB/T 528和GB/T 529，拉伸速率为500 mm·min-1。
Claims (1)
1.一种改性木质素/壳聚糖橡胶增强填料的制备方法，其特征在于，包括以下步骤：
S1.木质素的纯化：将木质素溶解于二氧六环-水溶液中，离心得到离心液，在离心液中滴加乙醚，得到沉淀，将沉淀洗涤干燥，得到纯化的木质素，其中二氧六环-水的体积比为9:1；
S2.木质素的氧化和磺化：将木质素加入至含有氢氧化钠的去离子水中，加热至木质素完全溶解，调节溶液的pH值至5，然后加入过氧化氢和硫酸亚铁反应，待达到反应时间后加碱调节溶液pH至9，加入甲醛和二乙醇胺，在70-80℃下反应后，再升温至90℃，加入亚硫酸钠，反应完全后，加酸使得木质素沉淀，洗涤干燥得到氧化磺化的木质素；
S3.木质素/壳聚糖的复合：将步骤S2中制备的木质素溶解于二氧六环-水的溶液配置浓度为3％的溶液，壳聚糖溶解于2-3％醋酸水溶液中配置浓度为2-5％的溶液，将两种溶液按体积比1:0.5-1.5混合，加入0.3-0.8％的戊二醛交联，最后在室温下抽滤，洗涤，并在红外箱中烘干，得到木质素/壳聚糖复合粉末；
S4.双硬脂酰乙基环氧丙基氯化铵的合成：将双硬脂酰基二乙烯三胺和苯加热回流反应，并滴加环氧氯丙烷，搅拌至反应完全后蒸发出苯和过量的环氧氯丙烷，得到双硬脂酰胺乙基环氧丙基氯化铵，其中，双硬脂酰基二乙烯三胺和环氧氯丙烷溶解于苯中的浓度为0.8-1mol/L；
S5.改性木质素/壳聚糖的制备：将步骤S3制备的木质素/壳聚糖复合粉末加入至去离子水水中配置成浓度为0.5mol/L的溶液，加热至40-50℃搅拌至完全溶解，调节pH为10，然后滴加双硬脂酰胺乙基环氧丙基氯化铵，搅拌下反应1-3h，再抽滤干燥，得到改性木质素/壳聚糖。