Wang et al., 2000 - Google Patents

Densification and properties of fluxed sintered NiCuZn ferrites

Wang et al., 2000

Document ID
3178577608367142890
Author
Wang S
Wang Y
Yang T
Wang P
Lu C
Publication year
Publication venue
Journal of magnetism and magnetic materials

External Links

Snippet

PbO· SiO2, PbO· B2O3 and Bi2O3 flux systems were used to lower the sintering temperature of an (Ni0. 38Cu0. 12Zn0. 50) Fe2O4 ferrite. The PbO· SiO2 glass system was found to be the most effective additive to obstruct the grain boundary movement and prevent the …
Continue reading at www.sciencedirect.com (other versions)

Classifications

    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3205—Alkaline earth oxides or oxide forming salts thereof, e.g. beryllium oxide
    • H—ELECTRICITY
    • H01—BASIC ELECTRIC ELEMENTS
    • H01F—MAGNETS; INDUCTANCES; TRANSFORMERS; SELECTION OF MATERIALS FOR THEIR MAGNETIC PROPERTIES
    • H01F1/00—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties
    • H01F1/01—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials
    • H01F1/03—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity
    • H01F1/12—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of soft-magnetic materials
    • H01F1/34—Non-metallic substances, e.g. ferrites
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/01—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics
    • C04B35/46—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on titanium oxide or titanates
    • C04B35/462—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on titanium oxide or titanates based on titanates
    • C04B35/465—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on titanium oxide or titanates based on titanates based on alkaline earth metal titanates
    • C04B35/468—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on titanium oxide or titanates based on titanates based on alkaline earth metal titanates based on barium titanates
    • C04B35/4682—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on titanium oxide or titanates based on titanates based on alkaline earth metal titanates based on barium titanates based on BaTiO3 perofskite phase
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3294—Antimony oxides, antimonates, antimonites or oxide forming salts thereof, indium antimonate
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3231—Refractory metal oxides, their mixed metal oxides, or oxide-forming salts thereof
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/01—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics
    • C04B35/26—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on ferrites
    • C04B35/2608—Compositions containing one or more ferrites of the group comprising manganese, zinc, nickel, copper or cobalt and one or more ferrites of the group comprising rare earth metals, alkali metals, alkaline earth metals or lead
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/626—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/34—Non-metal oxides, non-metal mixed oxides, or salts thereof that form the non-metal oxides upon heating, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3409—Boron oxide, borates, boric acids, or oxide forming salts thereof, e.g. borax
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/50—Constituents or additives of the starting mixture chosen for their shape or used because of their shape or their physical appearance
    • C04B2235/54—Particle size related information
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
    • C04B2235/74—Physical characteristics
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/65—Aspects relating to heat treatments of ceramic bodies such as green ceramics or pre-sintered ceramics, e.g. burning, sintering or melting processes
    • C04B2235/656—Aspects relating to heat treatments of ceramic bodies such as green ceramics or pre-sintered ceramics, e.g. burning, sintering or melting processes characterised by specific heating conditions during heat treatment
    • C04B2235/6565—Cooling rate
    • H—ELECTRICITY
    • H01—BASIC ELECTRIC ELEMENTS
    • H01F—MAGNETS; INDUCTANCES; TRANSFORMERS; SELECTION OF MATERIALS FOR THEIR MAGNETIC PROPERTIES
    • H01F41/00—Apparatus or processes specially adapted for manufacturing or assembling magnets, inductances or transformers; Apparatus or processes specially adapted for manufacturing materials characterised by their magnetic properties
    • H01F41/14—Apparatus or processes specially adapted for manufacturing or assembling magnets, inductances or transformers; Apparatus or processes specially adapted for manufacturing materials characterised by their magnetic properties for applying magnetic films to substrates

Similar Documents

Publication Publication Date Title
Wang et al. Densification and properties of fluxed sintered NiCuZn ferrites
Soman et al. Dielectric and magnetic properties of Mg–Ti substituted barium hexaferrite
Nakamura et al. Control of high-frequency permeability in polycrystalline (Ba, Co)-Z-type hexagonal ferrite
Qi et al. Effect of Mn substitution on the magnetic properties of MgCuZn ferrites
Wang et al. Densification and magnetic properties of low-fire NiCuZn ferrites
Lee et al. Low-loss Z-type hexaferrite (Ba3Co2Fe24O41) for GHz antenna applications
Hsu et al. The effect of V/sub 2/O/sub 5/on the sintering of NiCuZn ferrite
Yang et al. The magnetic and dielectric properties of microwave sintered yttrium iron garnet (YIG)
Li et al. Permeability spectra of planar M‐type barium hexaferrites with high Snoek’s product by two‐step sintering
Xu et al. Densification and magnetic properties of NiCuZn low-sintering temperature ferrites with Bi2O3-Nb2O5 composite additives
Tsay et al. Microwave sintering of (Bi0. 75Ca1. 2Y1. 05)(V0. 6Fe4. 4) O12 microwave magnetic materials
Bai et al. Magnetic properties of Cu, Zn-modified Co2Y hexaferrites
Ji et al. Enhanced electromagnetic properties of low-temperature sintered NiCuZn ferrites by doping with Bi2O3
Wang et al. Microstructures and high-frequency magnetic properties of low-temperature sintered Co–Ti substituted barium ferrites
Qinghui et al. Microstructure and magnetic properties of microwave sintered NiCuZn ferrite for application in LTCC devices
Xie et al. Low-temperature sintering and ferrimagnetic properties of LiZnTiMn ferrites with Bi2O3-CuO eutectic mixture
Su et al. Effects of Bi2O3–WO3 additives on sintering behaviors and magnetic properties of NiCuZn ferrites
Zhang et al. Magnetic and electrical properties of Z-type hexaferrites sintered in different atmospheres
Wang et al. Synthesis of Cu-modified Co2Z hexaferrite with planar structure by a citrate precursor method
Li et al. Suppressed domain wall damping in planar BaM hexaferrites for miniaturization of microwave devices
Wang et al. Effect of CaO–B2O3–SiO2 glass on the magnetic and dielectric properties of NiCuZn ferrites
Yang et al. Cd2+-enhanced the structure, electrical and magnetic properties of low-temperature sintered NiCuZn ferrites
Chen et al. Cold-sintered Ni0. 2Cu0. 2Zn0. 6Fe2O4-Li2MoO4 ceramic composites with enhanced magnetodielectric properties
Yue et al. Preparation and electromagnetic properties of ferrite–cordierite composites
Zhao et al. Effects of Bi2O3 and Li2OB2O3Bi2O3SiO2 glass on electromagnetic properties of NiCuZn/BaTiO3 composite material at low sintering temperature