Ibbott et al., 1995 - Google Patents
Further developments in the brazing of beryllium to CuCrZrIbbott et al., 1995
- Document ID
- 1414095959347705901
- Author
- Ibbott C
- Falter H
- Meurer P
- Thompson E
- Watson M
- Critchlow G
- Ciric D
- Publication year
- Publication venue
- Fusion Technology 1994
External Links
Snippet
We report on further studies and results relating to the development of induction brazing of beryllium to CuCrZr. This technology is of interest for water-cooled plasma facing components capable of continuous operation at power densities in the range S-ISMWm-z …
- 229910052790 beryllium 0 title abstract description 7
Classifications
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K20/00—Non-electric welding by applying impact or other pressure, with or without the application of heat, e.g. cladding or plating
- B23K20/02—Non-electric welding by applying impact or other pressure, with or without the application of heat, e.g. cladding or plating by means of a press; Diffusion bonding
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| US7361412B2 (en) | Nanostructured soldered or brazed joints made with reactive multilayer foils | |
| Barabash et al. | Armor and heat sink materials joining technologies development for ITER plasma facing components | |
| Ambekar | Additional studies on interface temperatures and bonding mechanisms of ultrasonic welds | |
| Davis et al. | Material properties and design requirements for copper alloys used in ITER | |
| Ibbott et al. | Further developments in the brazing of beryllium to CuCrZr | |
| Odegard Jr et al. | A review of the US joining technologies for plasma facing components in the ITER fusion reactor | |
| CN101048826A (en) | Single board cooling device component | |
| Cavalli et al. | Cohesive‐zone modelling of the deformation and fracture of spot‐welded joints | |
| EP0480962B1 (en) | Sodium/sulphur cells including a ceramic member and a metal member bonded together | |
| Kim et al. | Residual stress and plastic strain in AI51 304L stainless steel/titanium friction welds | |
| Kang et al. | Design of high-temperature brazing alloys for ceramic-metal joints | |
| JPH11190787A (en) | Heat resistant direct joint structure of high melting point material and high thermal conductivity material or jointing method therefor | |
| Šmid et al. | Performance of brazed graphite, carbon-fiber composite, and TZM materials for actively cooled structures: qualification tests | |
| Well | Low temperature large-area brazing of damage tolerant titanium structures | |
| Wei et al. | A damage-coupled TMF constitutive model for solder alloy | |
| Tvergaard | Effect of thermally induced residual stresses on the failure of a whisker-reinforced metal | |
| Zhou et al. | Determining mode-I cohesive parameters for nugget fracture in ultrasonic spot welds | |
| Vaziri et al. | Dynamic response of adhesively bonded single-lap joints with a void subjected to harmonic peeling loads | |
| Chow et al. | Damage mechanics characterization on the fatigue behaviour of a solder joint material | |
| Wetherhold et al. | Thermal cycling of tungsten-fibre-reinforced superalloy composites | |
| Van Heerden et al. | A tenfold reduction in interface thermal resistance for heat sink mounting | |
| Samadvand et al. | Near free-edge stresses in FRP-to-concrete bonded joint due to mechanical and thermal loads | |
| Bond et al. | Evolution of the SP‐100 conductively coupled thermoelectric cell | |
| Dudek et al. | In-situ solder fatigue studies using a thermal lap shear test | |
| Šmid et al. | Response to high heat fluxes and metallurgical examination of a brazed carbon-fiber-composite/refractory-metal divertor mock-up |