Aydin et al., 2019 - Google Patents

The effect of cement raw mix waste dust on porcelain tile properties

Aydin et al., 2019

View PDF
Document ID
10923022276435575060
Author
Aydin T
Paksoy C
Publication year
Publication venue
Journal of the Australian Ceramic Society

External Links

Snippet

Nowadays, the recycling of industrial waste is one of the priority issues. Recycling studies related with reducing the negative effects of wastes on the environment are becoming increasingly important. It was believed that nothing was beyond recycling, and …
Continue reading at www.academia.edu (PDF) (other versions)

Classifications

    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/327—Iron group oxides, their mixed metal oxides, or oxide-forming salts thereof
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3205—Alkaline earth oxides or oxide forming salts thereof, e.g. beryllium oxide
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/01—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics
    • C04B35/16—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on silicates other than clay
    • C04B35/18—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on silicates other than clay rich in aluminium oxide
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/34—Non-metal oxides, non-metal mixed oxides, or salts thereof that form the non-metal oxides upon heating, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3427—Silicates other than clay, e.g. water glass
    • C04B2235/3436—Alkaline earth metal silicates, e.g. barium silicate
    • C04B2235/3454—Calcium silicates, e.g. wollastonite
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/50—Constituents or additives of the starting mixture chosen for their shape or used because of their shape or their physical appearance
    • C04B2235/52—Constituents or additives characterised by their shapes
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/01—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics
    • C04B35/03—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on magnesium oxide, calcium oxide or oxide mixtures derived from dolomite
    • C04B35/04—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on magnesium oxide, calcium oxide or oxide mixtures derived from dolomite based on magnesium oxide
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/626—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
    • C04B2235/96—Properties of ceramic products, e.g. mechanical properties such as strength, toughness, wear resistance
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B28/00—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements
    • C04B28/02—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements containing hydraulic cements other than calcium sulfates
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2111/00—Mortars, concrete or artificial stone or mixtures to prepare them, characterised by specific function, property or use
    • C04B2111/00474—Uses not provided for elsewhere in C04B2111/00
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B7/00—Hydraulic cements
    • C04B7/12—Natural pozzuolanes; Natural pozzuolana cements; Artificial pozzuolanes or artificial pozzuolana cements other than those obtained from waste or combustion residues, e.g. burned clay; Treating inorganic materials to improve their pozzuolanic characteristics
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/65—Aspects relating to heat treatments of ceramic bodies such as green ceramics or pre-sintered ceramics, e.g. burning, sintering or melting processes
    • C04B2235/656—Aspects relating to heat treatments of ceramic bodies such as green ceramics or pre-sintered ceramics, e.g. burning, sintering or melting processes characterised by specific heating conditions during heat treatment
    • C04B2235/6565—Cooling rate
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B33/00—Clay-wares
    • C04B33/02—Preparing or treating the raw materials individually or as batches
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B14/00—Use of inorganic materials as fillers, e.g. pigments, for mortars, concrete or artificial stone; Treatment of inorganic materials specially adapted to enhance their filling properties in mortars, concrete or artificial stone
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B41/00—After-treatment of mortars, concrete, artificial stone or ceramics; Treatment of natural stone
    • C04B41/45—Coating or impregnating, e.g. injection in masonry, partial coating of green or fired ceramics, organic coating compositions for adhering together two concrete elements

Similar Documents

Publication Publication Date Title
Lavat et al. Characterization of ceramic roof tile wastes as pozzolanic admixture
Njindam et al. Effect of glass powder on the technological properties and microstructure of clay mixture for porcelain stoneware tiles manufacture
Luz et al. Use of glass waste as a raw material in porcelain stoneware tile mixtures
Hojamberdiev et al. Utilization of muscovite granite waste in the manufacture of ceramic tiles
Kłosek-Wawrzyn et al. Sintering behavior of kaolin with calcite
Abdel-Gawwad et al. A clean approach through sustainable utilization of cement kiln dust, hazardous lead-bearing, and sewage sludges in the production of lightweight bricks
García-Ten et al. Thermal conductivity of traditional ceramics: Part II: Influence of mineralogical composition
Andreola et al. Technological properties of glass-ceramic tiles obtained using rice husk ash as silica precursor
Chin et al. Relationship between the thermal behaviour of the clays and their mineralogical and chemical composition: Example of Ipoh, Kuala Rompin and Mersing (Malaysia)
Toya et al. Preparation and properties of glass-ceramics from wastes (Kira) of silica sand and kaolin clay refining
Aydin et al. Addition of cement kiln dust in ceramic wall tile bodies
Ochen et al. Physical and mechanical properties of porcelain tiles made from raw materials in Uganda
dos Santos Vazzoler et al. Investigation of the potential use of waste from ornamental stone processing after heat treatment for the production of cement-based paste
Aydin et al. The effect of cement raw mix waste dust on porcelain tile properties
Vasić et al. Raw kaolinitic–illitic clays as high-mechanical-performance hydraulically pressed refractories: MV Vasić et al.
Baspinar et al. Utilization potential of silica fume in fired clay bricks
Kritikaki et al. Valorization of industrial wastes for the production of glass–ceramics
Bahtli et al. The use of foundry waste sand from investment casting in the production of porcelain tiles
Vodova et al. The effect of CaO addition on mechanical properties of ceramic tiles
Salem et al. Shrinkage prediction during non-isothermal sintering in the presence liquid phase: New kinetic model, Part I
Ozturk Effect of addition of Avanos’s (Nevsehir) clays on the physical and microstructure properties of ceramic tile
Almeida et al. Thermal study of calcium silicate material synthesized with solid wastes
Das et al. The effect of basic oxygen furnace slag and Fly ash additions in triaxial porcelain composition: phase and micro structural evolution
Hamadou et al. Cement kiln dust in CIMENCAM Figuil (North Cameroon): characteristics and recycling as additives for blended cement production
Roushdy Recycling of the mixture resulted from sanitary ware waste, roller kiln waste and ceramic tiles sludge waste in the manufacturing of ceramic floor tiles