Failure analysis of a brazed, stainless steel fuel injection lineKral et al., 2018
View PDF- Document ID
- 9590076357867337539
- Author
- Kral M
- Maher C
- McSwain R
- Publication year
- Publication venue
- Engineering Failure Analysis
External Links
Snippet
An aircraft fuel line was found to have fractured and caused an in-flight fire. A brief history of the general problem of cracking in brazed stainless steel fuel injection lines places this failure in context. The fracture mechanism was likely to be fatigue due to vibrations. Other …
- 239000000446 fuel 0 title abstract description 97
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Krstic et al. | An investigation of the repetitive failure in an aircraft engine cylinder head | |
| Juarez et al. | Failure analysis of a diesel generator connecting rod | |
| Azadi et al. | Failure analysis of a cracked gasoline engine cylinder head | |
| Kral et al. | Failure analysis of a brazed, stainless steel fuel injection line | |
| Xu et al. | Failure analysis of a marine intermediate shaft | |
| Alam et al. | Failure analysis of a mobile crane: a case study | |
| Byrnes et al. | An unusual failure of a nickel-aluminium bronze (NAB) hydraulic valve | |
| Wang et al. | Failure analysis and improvement of a 42CrMo crankshaft for a heavy-duty truck | |
| Baumgartner et al. | Fatigue of brazed joints made of X5CrNi18-10 and Cu110 and derivation of reliable assessment approaches | |
| Oh | Bending fatigue and microstructure of fillet welded joints with high chromium stainless pipe for catalyst muffler | |
| Chandra et al. | Failure cases of stainless steel 316/316L pipe welds in moist hydrogen sulfide environment | |
| Nascimento et al. | Considerations on corrosion and weld repair effects on the fatigue strength of a steel structure critical to the flight-safety | |
| US8367964B2 (en) | Repair methods involving conductive heat resistance welding | |
| Bhavsar et al. | Effect of Compressed Natural Gas (CNG) on corrosion behaviour of brass valve of CNG cylinder | |
| Hussain et al. | Evaluation of Stress Relaxation Cracking on 800HT Pigtails of the Steam Reformer | |
| Ruminski | Examination of variable frequency drive transformer copper cooling line failures from nuclear power plants | |
| González et al. | Determination of the fracture cause in an aircraft motor cylinder | |
| Krstic et al. | Fatigue as a cause of failure of aircraft engine cylinder head | |
| Didenko et al. | Turbine shroud cracking investigation and repair | |
| Belben | Failure investigations of helicopter tail rotor gearbox casings at agustawestland limited | |
| Morrison et al. | Investigation of a failed stainless steel spindle assembly | |
| Alias et al. | Failure Analysis of a Carbon Steel Pipe-Flange Component | |
| Muhammad et al. | FAILURE ANALYSIS OF HYDROGEN EMBRITTLEMENT IN SHIP GEARBOX HEX BOLTS. | |
| Shahin et al. | Analysis of a Chain Conveyor Link Failure | |
| Liu et al. | Effect of high temperature exposure on the mechanical properties of cold expanded open holes in 7050-T7451 aluminium alloy |