Corrosion-Fatigue Failure of A Marine Propeller ShaftZAPFFE, 1953
- Document ID
- 7407251334259954841
- Author
- ZAPFFE C
- Publication year
- Publication venue
- Corrosion
External Links
Snippet
An ususually clear example of corrosion-fatigue failure is used as a basis for discussing those forms of fracture in which chemical attack combines with mechanical stress to destroy an engineering structure. The term “mechanochemical” is introduced to cover the entire …
- 239000000126 substance 0 abstract description 12
Classifications
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Cragnolino et al. | Intergranular stress corrosion cracking of austenitic stainless steel at temperatures below 100 C—a review | |
| Gaul et al. | The effect of fretting and environment on fatigue crack initiation and early propagation in a quenched and tempered 4130 steel | |
| Nielsen | OBSERVATIONS AND THOUGHTS ON STRESS CORROSION MECHANISMS ASTM 1970 GILLETT MEMORIAL LECTURE | |
| Gallagher | Corrosion fatigue crack growth rate behavior above and below K sub Iscc in steels(Corrosion fatigue cyclic crack growth rate above and below environmental threshold stress in steels as function of frequency and potentials, indicating hydrogen embrittlement) | |
| EP0404788A1 (en) | Metallic surface protection | |
| Henthorne | Corrosion of resulfurized free-machining stainless steels | |
| ZAPFFE | Corrosion-Fatigue Failure of A Marine Propeller Shaft | |
| Vermilyea | A film rupture model for stress corrosion cracking | |
| Tiner et al. | Microprocesses in Stress Corrosion of Martensitic Steels | |
| Ogino et al. | Effect of amplitude on erosion-corrosion of metals by vibratory cavitation in relation to pH of the cavitation media | |
| Kwon et al. | Effects of flow rate on crack growth in sensitized type 304 stainless steel in high-temperature aqueous solutions | |
| Desjardins et al. | Mechanism of Stress-Corrosion Cracking of Stainless Steels in Hot Chloride Media: Influence of Work Hardening | |
| Bruemmer et al. | Evaluating the Intergranular SCC Resistance of Sensitized Type 304 Stainless Steel in Low-Temperature Water Environments | |
| Waber et al. | Theory of Stress Corrosion Cracking of Mild Steel in Nitrate Solutions | |
| Lackey et al. | Intergranular Stress Corrosion Cracking of Sensitized Austenitic Stainless Steel--a Microcompositional and Structural Investigation | |
| SU583200A1 (en) | Method of chemical and heat treatment of ferrochromium electrical steels | |
| Sarafian | Influence of microstructure on stress corrosion cracking of mild steel in synthetic caustic-nitrate nuclear waste solution | |
| Hart | Stress-Corrosion Cracking of Cast Iron—Nickel—Chromium Alloys | |
| Uhlig | Stress-corrosion cracking | |
| Kalidindi | Pitting and Stress Corrosion Cracking in Alloy 200� | |
| Higgins | Evaluation of susceptibility of AISI 304 to stress-corrosion cracking in terms of crack nucleation and crack propagation | |
| Iwabuchi | Effect of nitrogen and delta-ferrite contents on mechanical properties, corrosion resistance and abrasive wear in type SCS 13 stainless cast steel | |
| WILLIAMS | Stress-Corrosion Cracking: A Review of Current Status | |
| Masuda | The Stress Corrosion Cracking Behaviour of Weldment in Austenitic and Austenitic-ferritic Stainless Steels | |
| Tshilwane | The environmentally assisted cracking of Ru enriched laser alloyed surface layers on 304L stainless steel |